Aluminum Strip Casting

Sumário:

Aluminum strip casting is a key contributor to weight saving possibilities, particularly in the automotive industry and although strip casting has been established for over 50 years, it continues to increase in popularity.
Casting speeds can be limited by several factors including the type of alloy being cast and the desired sheet thickness required.

In the automotive industry, decreasing weight is one of the most important challenges which needs to be solved and using aluminum alloys instead of the more traditional steels enables a great opportunity to decrease weight substantially of the overall vehicle.

However, sheets of aluminum alloy used for automobile body work are very expensive. Therefore, in order to make use of aluminum alloys cost effective it is necessary to develop a low cost aluminum alloy sheet which can handle the intended application requirements.

The development of continuous casters for aluminum products has been well documented over the past 50 years. Processes are classified according to the thickness that can be produced using either thin slab or strip casting. Thin slab and thin strip casting bypasses the semi-finished product stage, reducing reheating and eliminating a number of rolling steps, thus providing for considerable energy savings and significant improvements in productivity.

Strip casting was commercialized in the early 1950s. Aluminum alloy sheets are mainly produced in a twin roll caster. In this process, the molten metal is introduced between a pair of counter rotating horizontal casting rolls wherein solidification is initiated when the molten metal contacts the rolls. The solid metal shell formed on the roll surface advances toward the point of minimum clearance between the rolls, referred to as the nip. When the metal passes through the nip, solidification is fully completed and the material undergoes deformation as it exits the rolls. Low alloyed aluminum alloys have successfully been strip cast at a thicknesses of ¼ inch at rolling speeds of 4 to 6 feet/min (50 to 70 lbs/hr/in).



Figure 1: Aluminum Strip casting

The casting speed is restricted by the fact that an increase in casting speed will increase centerline segregation in the sheet. In particular, the central zone of the sheet will become enriched with eutectic forming elements (Fe, Si, Ni, Zn) and depleted in peritectic forming elements (Ti, Cr, V, Zr).

Therefore, more highly alloyed materials (e.g. AA5XXX and 6XXX) are more difficult to produce by the strip casting process. Another aspect of the process is that the high separation force required to achieve the desired sheet thickness further limits the casting speed. This is because the aluminum strip is solid when it enters the nip, resulting in a required force of several tons per inch width. Difficulty in achieving uniform heat transfer as rolling speed increases also represents another impediment to increasing process speed. Commercial strip casters can produce strips with thicknesses ranging from 1 to 15 mm.



Figure 2: Microstructures of twin-roll continuous cast aluminum thin strip: (a) Solidified organization on cross section of aluminum strip; (b) Local magnification of (a)


References

1. H. Sakaguchi, T. Haga, H Watari, S. Kumai: High speed twin roll casting of 6016 aluminium alloy strip, Journal of Achievements in Materials and Manufacturing Engineering, Vol.20, Issue 1-2, January-February 2007, p.495-498;

2. T. Haga, M. Ikawa; H. Watari, K. Suzuki, S. Kumai: High-Speed Twin Roll Casting of Thin Aluminum Alloy Strips Containing Fe Impurities, Materials Transactions, Vol. 46, No. 12, 2005, p. 2596-2601;

3. B. Davis, J. Hryn: Innovative Forming and Fabrication Technologies: New Opportunities, ARGONE, Final Report, 15 Decembre 2007, K. Suzuki, S. Kumai, Y. Saito and T. Haga: High-Speed Twin-Roll Strip Casting of Al–Mg–Si Alloys with High Iron Content, Materials Transactions, Vol. 46, No. 12, 2005, p. 2602- 2608;

4. Horizontal continuous casting in graphite mold, Accessed Sept 2016;

5. Chen Shou-dong, et al.: Simulation of microstructures in solidification of aluminum twin-roll casting, Trans. Nonferrous Met. Soc. China 22, 2012, p.1452−1456;

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

O banco de dados da Total Materia contém muitos milhares de materiais de alumínio através de uma grande variedade de países e padrões.

Quando disponíveis, informações de propriedade completa pode ser vista de materiais incluindo a composição química, propriedades mecânicas, propriedades físicas, dados de propriedades avançadas e muito mais.

Usando a página de pesquisa avançada, definir os critérios de pesquisa, selecionando "Alumínio" no Grupo de Materiais lista pop-up. É talvez o que você precisa para estreitar ainda mais os critérios de pesquisa usando os campos na página de pesquisa avançada por exemplo, País / Standard.

Em seguida, clique em Enviar.


Uma lista de materiais será então gerado para você escolher.


Depois de clicar em um material a partir da lista resultante, uma lista de subgrupos derivados de especificações padrão aparece.

A partir daqui é possível ver os dados de propriedades específicas para o material selecionado e também para ver os materiais semelhantes e equivalentes em nossas poderosas tabelas de referência cruzada.


Clique no link de dados propriedade de seu interesse para ver os dados de propriedade específicos.




Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.