Rapid Slurry Forming (RSF) Technology

Sažetak:

Rapid slurry formation (RSF) is a novel semi-solid metal forming technique which allows complex geometries to be formed in a single operation.
Advantages of RSF include a much reduced suspension preparation time and cost and most importantly the ability to achieve a globular structure and high fluidity of suspension at the same time.

Rapid slurry formation is a semi-solid metal forming technique, which is based on a so-called solid enthalpy exchange material (EEM). It is a fascinating technology offering the opportunity to manufacture net-shaped metal components of complex geometry in a single forming operation.

The RSF process differs from other rheocasting processes because heat extraction and temperature control are not necessary. The RSF process is based on enthalpy exchange of two alloys where one alloy is the low superheat melt (high enthalpy).

The other one acts as the cold solid stirring material (low enthalpy) and is also known as enthalpy exchange material (EEM). During the process the EEM is submerged into the melt while stirring action is applied. Heat is absorbed from the melt during stirring operation, and the two alloys with different enthalpies will form a new alloy system with a new enthalpy level.

RSF technology is able to extract a very large amount of heat through enthalpy exchange of similar material in a very short time. This also improves the castability of the alloy significantly. The reason being that through RSF technology, the morphology of the primary phase changes from coarse dendrites to near globular, which eliminates the feeding problem during solidification that is associated with conventional casting method.

The advantage of the method is that the relatively low solid phase fraction (20-30%) provides for achieving a globular structure with simultaneous retaining the high fluidity of suspension, and the preparation of the suspension is much shorter and cheaper than for other methods.



Figure 1: Schematic diagram of heat exchange during slurry formation in RSF process

Figure 2(a) exhibits the typical as-cast structure of A 357 alloy where highly dendritic α-Al phase is present. Whereas Fig. 2(b-f) show semi-solid structures of A357 alloy at different rpm. One can see change in dendritic morphology of α-Al in semi-solid structure. This improves the castability of the alloy significantly. The reason being that through RSF technology, the morphology of the primary phase changes from coarse dendrites to near globular, which eliminates the feeding problem during solidification that is associated with conventional casting method.



Figure 2: Optical Microstructures of A357 alloy at different rotation speed: (a) 0 rpm, (b) 450 rpm, (c) 800 rpm, (d) 1200 rpm, (e) 1400 rpm and (f) 1800 rpm


References

1. L.Ratke, A.Sharma, D.Kohli: Effect of process parameters on properties of Al-Si alloys cast by Rapid Slurry Formation (RSF) technique, IOP Conf. Series: Materials Science and Engineering 27 (2011) 012068 doi:10.1088/1757-899X/27/1/012068;

2. A.Sharma: Synthesis of semi solid slurry and effect of inoculants on microstructure of A356 alloy cast by rapid slurry forming (rSF) process, La Metallurgia Italiana - n. 4/2013, p.53-58;

3. Z.Konopka, M.Lagiewka, M.Nadolski, A.Zyska: Theoretical analysis of the AlSi10Mg alloy suspension manufacturing by the RSF process, Archives of Metallurgy and Materials, Vol.55, Issue 3, 2010, p.869-873;

4. L.Ratke, A.Sharma, D.Kohli: The RSF Technology for Semi-Solid Casting Processes, Technical Paper, Indian Foundry Journal, Vol.57, No10. October 2011, p.33-36

Pretražite bazu znanja

Unesite reč za pretragu:

Pretražite prema

Kompletan tekst
Ključne reči

Naslovi
Sažetak

U Total Materia bazi se nalazi više hiljada metalografskih snimaka poreklom iz različitih zemalja i standarda.

Korišćenjem kartice Metalografija u meniju možete izabrati materijal koji Vas zanima iz liste materijala koji sadrže metalografske podatke.

Metalografske podatke možete naći i kroz našu standardnu Brzu pretragu, a svi dostupni podaci biće prikazani listom podgrupa za odabrani materijal.

Jednostavno unesite oznaku materijala u polje Materijal, odaberite standard, ako je poznat, pa kliknite Pretražite.

solution img

Opšte informacije o mikrostukturi možete videti zajedno sa odgovarajućim hemijskim sastavom za odabrani materijal.

solution img

Za određene materijale postoje metalogafski snimci pri različitim uvećanjima.

Možete odabrati druga stanja iz padajućeg menija Izaberite stanje da biste videli metalografske snimke iz drugih procesa i pri različitim vidovima termičke obrade.

solution img

solution img

Imate priliku da isprobate Total Materia bazu podataka. Pozivamo Vas da se pridružite zajednici od preko 150,000 registrovanih korisnika kroz Total Materia Besplatan demo.