High Chromium Cast Iron: Part One


High chromium cast irons (HCCI’s) exhibit very good mechanical properties and offer benefits for a range of manufacturing applications.
With carefully controlled heat treatment the cast iron properties can be further influenced to yield higher strength and ductility depending on the desired application.

High-chromium white iron is an erosion resistant ferrous alloy widely used in manufacturing, it has for long been applied to components in mining and minerals industry due to its excellent abrasion resistance, imparted by the hard alloy eutectic carbides present in the microstructure. Furthermore heat treatment can improve properties, all of interest, depending upon the particular applications.

High-chromium irons have good mechanical properties, high hardness in a cast state, low fluctuation of hardness when properties change. High-chromium irons almost don’t concede in fluidity to regular gray cast iron that allows using parts sufficiently difficult form directly after casting without the following machining.

Table 1: Chemical composition of high-chromium wear resistant irons

The mechanical properties of High chromium cast iron HCCI mainly depend on type, size, number, morphology of hard carbides and the matrix structure (γ or α). The hypereutectic HCCI with large volume fractions of hard carbides is preferred to apply in wear applications. However, the coarser and larger primary M7C3 carbides will be precipitated during the solidification of the hypereutectic alloy and these will have a negative influence on the wear resistance.

As mentioned above, high chromium cast irons (HCCIs) are mainly used in mining, milling, earth-handling and manufacturing industries which require materials with exceptional wear and corrosion resistance. The exceptional wear resistance of high chromium cast irons is due to the high volume fraction of hard chromium carbides, although the toughness of the matrix also contributes to the wear resistance. The high controlled percentage of chromium helps to retard the formation of graphite and stabilize the carbides.

The article of D. Kopyciński et al. presents results of heat treatment on the high chromium cast iron. The study was carrying out on samples cut from the casting made from chromium cast iron. Those were hardened at different temperatures, then tempered and soft annealed.

Hardness was measured at three points sample, and two at the edges. Figures 1 and 2 show results of hardness after hardening, tempering Vickers and Rockwell method respectively hardness of as-cast sample.

Test results indicate that with proper selection of heat treatment parameters the hardness and composition of phase microstructure of chromium cast iron can be controlled. Hardening affects positively the hardness of castings, whereas tempering and soft annealing improves ductile properties of chromium cast iron. By adjusting the heat treatment parameters, the material properties can be customized for a particular application. The studies let to determinate the optimum heat treatment for this type of cast iron. The best properties were obtained for hardening at 950°C, for other temperature of heat treatments the hardness increased and exceeded 60 HRC units.

Table 2: Heat treatment parameters for individual samples

Figure 1: The Vickers hardness of the samples tempering and soft annealing, and as-cast

Figure 2: The Rockwell hardness of the samples after hardening, tempering and soft annealing, and as-cast


1. N. Poolthong, H. Nomura, M. Takita: Effect of Heat Treatment on Microstructure and Properties of Semi-solid Chromium Cast Iron, Materials Transactions, Vol. 45, No. 3, 2004,p. 880- 887;

2. Sv.S.Kvon, V.Y.Kulikov, T.S.Filippova, E.E.Omarova: Using high-chromium iron as material for production of the equipping components of mine shafts, METALURGIJA, METABK 55,(2),2016, p. 206-208, ISSN 0543-5846;

3. Q.Liu: Microstructure evaluation and wear-resistant properties of Ti-alloyed hypereutectic high chromium cast iron, Doctoral Dissertation, Stockholm 2013, ISBN 978-91-7501-842-3;

4. N. Hussain, A. Kumar, P. Vijayanand: Mechanical Property and Microstructural Variation in Semi-Solid Processed High Chromium Cast Iron, International Journal of Engineering Research & Technology (IJERT), Vol. 3 Issue 7, July – 2014, ISSN: 2278-0181;

5. D. Kopyciński, E. Guzik, D. Siekaniec, A. Szczęsny: Analysis of the High Chromium Cast Iron Microstructure after the Heat Treatment, Archives of Foundry Engineering, Volume 14, Issue 3, 2014, p.43-46,ISSN 1897-3310;

Søg i Vidensbasen

Skriv en sætning for at søge efter:

Søg ud fra

Fuld tekst


Total Materia has mechanical properties inserted for many thousands of materials and accessing them is just a click of a button away.

Covering a wide variety of property information, it is easy to find yield stress, tensile stress and elongation data for a huge number of materials within the database.

Enter the material of interest into the quick search field. You can optionally narrow your search by specifying the country/standard of choice in the designated field and click Search.

solution img

Total Materia will generate the search list for you to select the material of interest from the material list.
Click on the material of interest.

solution img

On the subgroup page, click the Mechanical Properties link to view property data for the selected material. The number of mechanical property data records is displayed in brackets next to the link.

solution img

The mechanical properties data will be then be displayed along with all selected material information for your reference.

The mechanical properties data will be displayed for all available conditions and treatments.

solution img

It is also possible to switch between metric (SI) and Anglo-Saxon units with one click depending on your preference.

solution img

For you’re a chance to take a test drive of the Total Materia database, we invite you to join a community of over 150,000 registered users through the Total Materia Free Demo.