Engineering Stress-strain Curve: Part One

Sommario:

The engineering tension test is widely used to provide basic design information on the strength of materials and as an acceptance test for the specification of materials. In the tension test a specimen is subjected to a continually increasing uniaxial tensile force while simultaneous observations are made of the elongation of the specimen.

The shape and magnitude of the stress-strain curve of a metal will depend on its composition, heat treatment, prior history of plastic deformation, and the strain rate, temperature, and state of stress imposed during the testing. The parameters, which are used to describe the stress-strain curve of a metal, are the tensile strength, yield strength or yield point, percent elongation, and reduction of area. The first two are strength parameters; the last two indicate ductility.

An example of the engineering stress-strain curve for a typical engineering alloy is shown in Figure 1. From it some very important properties can be determined. The elastic modulus, the yield strength, the ultimate tensile strength, and the fracture strain are all clearly exhibited in an accurately constructed stress strain curve.


Figure 1: An example of the engineering stress strain curve for a typical engineering alloy

The elastic modulus, E (Young’s modulus) is the slope of the elastic portion of the curve (the steep, linear region) because E is the proportionality constant relating stress and strain during elastic deformation: σ = Eε.

The 0.2% offset yield strength is the stress value, σ0.2%YS of the intersection of a line (called the offset) constructed parallel to the elastic portion of the curve but offset to the right by a strain of 0.002. It represents the onset of plastic deformation.

The ultimate tensile strength is the engineering stress value or σuts, at the maximum of the engineering stress-strain curve. It represents the maximum load, for that original area, that the sample can sustain without undergoing the instability of necking, which will lead inexorably to fracture.

The fracture strain is the engineering strain value at which fracture occurred.

At the outset, though, a clear distinction must be made between a true stress-true strain curve and an engineering stress-engineering strain curve. The difference is shown in Figure 2, which are plotted, on the same axes, the stress-strain curve and engineering stress-strain curve for the same material. The difference is also evident in the definitions of true stress-true strain and engineering stress-engineering strain.


Figure 2: Comparison of engineering and true stress-strain curves

The engineering stress is the load borne by the sample divided by a constant, the original area. The true stress is the load borne by the sample divided by a variable the instantaneous area. Note that the true stress always rises in the plastic, whereas the engineering stress rises and then falls after going through a maximum.

The maximum represents a significant difference between the engineering stress-strain curve and the true stress-strain curve. In the engineering stress-strain curve, this point indicates the beginning of necking. The ultimate tensile strength is the maximum load measured in the tension test divided by the original area.

Criteri di ricerca
Inserite il vostro testo in inglese per la ricerca:

Ricerca tramite

Ricerca tramite

Testo completo
Intestazioni

Articolo
Sommario

Questo Articolo fa parte di una serie di Articoli di tecnologia metallurgica. È possibile fare clic sui link qui sotto per saperne di più su questo argomento.

Il Modulo opzionale Extended Range di Total Materia include una raccolta unica al mondo di curve Stress-Strain per calcoli in campo plastico relativi a migliaia di leghe metalliche, per differenti Trattamenti Termici e temperature di lavoro. Curve "true" e "engineering" sono fornite per varie velocità di deformazione ove applicabili.

Trovare un grafico Stress-Strain nel database è semplice e richiede solo pochi secondi.

Per prima cosa occorre inserire la Designazione della lega che interessa nel campo di Ricerca Rapida. Opzionalmente si può restringere la ricerca selezionando il Paese / Normativa dalla lista a discesa, e poi si clicca su "Invio".


Dopo aver selezionato il materiale di interesse, occorre cliccare sul collegamento "Curve Stress-Strain" per visualizzare i dati relativi al materiale selezionato. Il numero dei dati (diagrammi) disponibili viene visualizzato tra parentesi accanto al link.


Perché le curve Stress-Strain sono neutrali rispetto alle Normative, è possibile visualizzare i diagrammi cliccando sul link relativo per ogni Sottogruppo.

Oltre le curve Stress-Strain a diverse temperature, i dati sono forniti in forma di tabella che è esportabile a un software CAE come testo.


È anche possibile visualizzare curve Stress-Strain e relativi dati numerici per diverse temperature di lavoro.

Per fare questo, è sufficiente inserire una nuova temperatura nella casella specifica compresa nei limiti definiti e dare Invio.

Dopo aver fatto clic sul pulsante "Calcola", viene generata una nuova curva e i valori nella tabella corrispondono ora alla nuova temperatura. Si veda l'esempio qui sotto per 250°C.


Per consentirvi di testare il Database Total Materia "senza impegno", vi invitiamo a unirvi alla comunità degli Utenti registrati per i test gratuiti a Total Materia.