Low Temperature Carburizing of Austenitic Stainless Steel: Part One

概要:

Although austenitic stainless steels are among the most commonly applied corrosion resistant steels challenges exist related to their relatively poor surface hardness and wear resistance.
Low temperature carburizing presents an effective solution to these challenges by increasing surface hardness through a carbon rich diffusion zone which does not compromise the corrosion resistance of the material.

Austenitic stainless steels are the most widely used corrosion-resistant materials in various sectors of industries, due to their excellent chemical and metallurgical properties. However, they are notorious for their poor friction and wear characteristics. Attempts have been made during the past decades to engineer the surfaces of this type of materials so as to improve their surface hardness and wear resistance.

Surface Engineering treatments for austenitic stainless steel are an interesting alternative way to increase the surface hardness and improve the wear resistance. It is nowadays widely accepted that hard, wear and corrosion resistant surface layers can be produced on ASS by means low temperature nitriding and/or carburizing in a number of different media (salt bath, gas or plasma), each medium having its own strengths and weaknesses. In order to retain the corrosion resistance of austenitic stainless steel, these processes are typically conducted at temperatures below 450°C and 500°C, for nitriding and carburizing respectively. The result is a layer of precipitation free austenite, supersaturated with nitrogen and/or carbon, which is usually referred to as S- phase or expanded austenite.

Some industrially proven processes work at lower temperatures. They have a hardening effect without affecting the original corrosion resistance-providing the base material is good quality. No coating is applied to the surface, but a carbon-rich (up to 2-3% weight rate) diffusion zone is produced from the surface inwards, with excellent toughness and no risk of delamination or peeling. It is low-temperature carburizing, at a diffusion temperature below 450°C.

The process increases the surface hardness of most austenitic stainless steels to a level of about 1000-1200 HV0.05, which is about five times the original hardness. High compressive stresses are formed on the surface, due to interstitial solution of carbon atoms. All austenitic stainless steels can be hardened using this process. The process has also been successfully applied to duplex and precipitation hardening stainless steel grades. Materials to be treated by low-temperature carburizing should be in the solution annealed condition. Sharp edges, the inside of bores and gaps present no limitation to the process.

Low-temperature gas-phase carburization dramatically improves the hardness, wear resistance and corrosion resistance of austenitic stainless steels. However, successful application of this technology requires in situ removal of the spontaneously formed Cr2O3-rich passive film which otherwise inhibits or prevents uptake of carbon during carburization.

On electropolished surfaces of AISI 316L steel, a 16 hour acetylene-based carburization treatment at 450°C generated a continuous case (hardened surface layer) with up to 15 at.% carbon and >3% lattice parameter expansion. This increased the surface hardness from 3.5 GPa to 13 GPa. As in earlier observations on 316L after activation with a different method, acetylene-based carburization produced a colossal supersaturation of the austenite with carbon, even though needle-shaped carbide particles were observed on the specific processing conditions applied here. The stoichiometry of the carbides was M7C3, which demonstrated a specific orientation relationship with the austenite matrix. Despite the presence of carbide precipitates, the pitting corrosion resistance of the material in the chlorine-containing environments was significantly improved.

In the work of Y.Ge was revealed a strong influence of surface finish on the efficacy of low temperature acetylene-based carburization of AISI 316L. Finer finished samples obtained thicker cases and larger surface carbon concentrations than coarser finished samples. TEM (transmission electron microscopy) revealed that the difference is due to the deformation-induced disturbed layers on the steel surfaces. A thick (>400 µm) disturbed layer consisting of fine nano-crystalline grains (≈10 µm diameter) inhibits acetylene-based carburization. Systematic experiments demonstrated that low temperature carburization is more effective after removal of this layer.

In addition to carburization, low-temperature acetylene-based nitrocarburization was achieved by adding a small amount of ammonia gas to the carbonaceous gas mixture. The effects of temperature and gas composition on the acetylene-based carburization/nitrocarburization were also studied. It was found that adding nitrogen to the gas can suppress carbide precipitation without compromising the properties of such interstitially hardened steel.



Figure 1:SEM micrographs of 450°C carburised 8 h specimen


References

1. Y. Sun: Kinetics of low temperature plasma carburizing of austenitic stainless steels, Journal of Materials Processing Technology 168, 2005, p.189–194;
2. A. Triwiyanto, P. Husain, E. Haruman, M. Ismail: Low Temperature Thermochemical Treatments of Austenitic Stainless Steel Without Impairing Its Corrosion Resistance, Corrosion Resistance, Dr. Shih (Ed.), 2012, ISBN: 978-953-51-0467-4;
3. A.Kosmač: Surface Hardening of Stainless Steels, Second edition 2015, Materials and Applications Series, Volume 20, Euro Inox, ISBN 978-2-87997-395-1;
4. Y. Ge: Low-Temperature acetylene based carburization and nitrocarburizing of 316L austenitic stainless steel, PhD thesis, Case Western Reserve University, August 2013.

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

Total Materiaデータベースは世界の国々と広範な規格に関する数千種類のステンレス鋼材料に関するデータを収録しております。

必要に応じて、化学組成分、機械的特性、物理特性、高度な特性等々の材料特性を御覧になれます。

高度な検索のページでフルテキスト(完全一致)検索機能を使い一般的な用途ごとに材料を探す事が可能です。

さらに国/規格のフィールドを使い検索条件を絞ることもできます。

確定をクリックします。


選んだ材料の材料リストが表示されます。


結果リストで材料をクリックすると規格から導きだされるサブグループリストが表示されます。


そこから選んだ材料の特性を見る事ができさらにパワフルな相互参照表により類似材料、同等材料をみることもできます。

例えば、サブグループページの化学組成分のリンクをクリックするとその材料の化学組成分を見る事ができます。


ステンレス鋼材料の他の重要な特性すなわち機械的特性、物理特性、その他の高度な特性などもみることができます。


Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。